The M-51 wear-resistant coating is a high-performance wear-resistant and impact-resistant polymer material obtained by the combination of high-performance wear-resistant aggregates(Silicon Carbide, diamond sand, etc.) and special polymer materials. It is used to repair the surface wear of the drum of the magnetic separator or to make wear-resistant and impact-resistant coating directly on the surface of the drum.
Two-component, black or blue slime. It can be cured at room temperature, and better comprehensive performance can be obtained by heating and curing.
It has excellent bonding strength with metal substrates.
Scratchy, easy to shape, Shigongfangbian. After curing, the coating has excellent water resistance and aging resistance.
Excellent wear resistance and impact resistance; The impact resistance is 3 to 5 times that of imported wear-resistant protective agents。
Surface treatment: rough treatment of the parts to be treated(sandblasting treatment effect is better, if there is no sandblasting conditions can also be polished by the corner grinder); Cleaning and drying of roughened surface cleaning agents(available as acetone, ethyl acetate, etc.); The treated surface should be a rough, clean, fresh metal substrate.
Preparation: Press A: B = 4:1 to mix the A and B components evenly and use them up in 30 min. Generally, the construction side configuration, the maximum amount of one configuration can not exceed 3kilograms, one configuration too many glue, cure speed, has not been partially cured and can not be used.
Apply: It is recommended that the thickness of the coating is 3 to 6 mm, and the mixed material is applied to the bottom coating surface. The adhesive layer should be compacted. The coating is applied to the desired size and the surface is repaired.
Curing: Curing at 25 °C can be put into use for 24 hours; When the temperature is below 15 °C, heat should be used to promote curing. Heating conditions as high as 80 °C after curing at room temperature for 2 hours, coatingPerformance can be improved by 30 %.
耐磨抗冲击性能优异，专用于磁选机滚筒、破碎机、管道修补、选矿设备耐磨层、输料系统、弯头耐磨修补等金属设备的防磨保护。 The wear resistance and impact resistance performance is excellent, and it is specially used for wear protection of metal equipment such as magnetic separator drum, Crusher, pipe repair, abrasive layer of mineral processing equipment, material transmission system, and bending wear resistance repair.