The M-52 flotation groove repair special wear resistant adhesive is a high-performance wear resistant polymer material obtained by the combination of high-performance wear resistant particles(Silicon Carbide, diamond sand, etc.) and modified toughened wear resistant resin. It is widely used to repair the corrosion of pharmaceutical agents in flotation tanks and the abrasion caused by mineral particles. It can also be used to prepare wear-resistant anti-corrosion preprotective coatings directly on the inner wall of flotation tanks.
High binding strength for metal and resin substrates
No, no, no, Shigongfangbian.
Soaking resistance, acid-base resistance
Good toughness, no cracking, excellent wear resistance and corrosion resistance
Surface treatment: rough treatment of the parts to be treated(sandblasting treatment effect is better, if there is no sandblasting conditions can also be polished by the corner grinder); Cleaning and drying of roughened surface cleaning agents(available as acetone, ethyl acetate, etc.); The treated surface should be a rough, clean, fresh metal substrate.
Preparation: Press A: B = 4:1 to mix the A and B components evenly and use them up in 30 min. Generally, the construction side configuration, the maximum amount of one configuration can not exceed 3 kilograms, one configuration too many glue, cure speed, has not been partially cured and can not be used.
Apply: It is recommended that the thickness of the coating is 3 to 6 mm, and the mixed material is applied to the bottom coating surface. The adhesive layer should be compacted. The coating is applied to the desired size and the surface is repaired.
Curing: Curing at 25 °C can be put into use for 24 hours; When the temperature is below 15 °C, heat should be used to promote curing. Heating conditions in room temperature curing as far as possible 80 °C insulation for 2 hours, coating performance can be improved by 30 %.
It can be used to repair the corrosion of pharmaceutical agents and the abrasion caused by mineral particles in the flotation tank. It can also be used to prepare wear-resistant and anti-corrosion pre-protective coatings directly on the inner wall of the flotation tank.